XTCERA 3D Zirconia
Xtcera’s 3D Zirconia is graduated in translucency and strength from cervical to incisal to bring you the most natural looking aesthetics possible form a zirconia restoration. Intended for use with single units up to three-unit bridges, this material exhibits a natural translucence at the incisal of 55% with 750MPa of strength transitioning beautifully to a margin translucence of 47%-49% with strengths up to 1200MPa.
Beautiful aesthetics and structural integrity; a combination long desired in zirconia applications now available in 3D white with FREE water-based color liquids or 3D Multilayered (pre-shaded) in 16 Vita Classic shades and OM3 bleach shade.
Technical Data:
| XTCERA ZIRCONIA FAMILY | 3D MULTILAYER | 3D White |
| Transmittance (Translucency) | 55% (Incisal) – 43% (Cervical) | 55% (Incisal) – 43% (Cervical) |
| Available Shades | VITA Classic 16 Shadeds A1-D4 & OM3 | Color Liquids |
| Powder | High Quality Chinese | High Quality Chinese |
| Manufacturing Type | Axial Press->Isostatic Press->Sintering | Axial Press->Isostatic Press->Sintering |
| Physical Property | Physical Property | Physical Property |
| Bending Strength | INCISAL ≥750MPa – CERVICAL ≥1100MPa | INCISAL ≥750MPa – CERVICAL ≥1100MPa |
| Pre-Sintered Density | 3.06g/cm³ | 3.06g/cm³ |
| Sintered Density | ≥6.03g/cm³ | ≥6.04g/cm³ |
| Vickers Hardness | 1250HV | 1250HV |
| Chemical Solubility | <100μg/cm² | <100μg/cm² |
| CTE | 9.91×10 K | 9.91×10 K |
| Thermal Shock Resistence (YY0301-1998) | Complied | Complied |
| Chemical Composition | Chemical Composition | Chemical Composition |
| ZrO2+HfO2 | >94% | >94% |
| Y2O3 | 4.5-6.0wt% | 4.5-6.0wt% |
| AL2O3 | <0.5wt% | <0.5wt% |
| Other Oxides | < 0.5wt% | < 0.5wt% |